WELDING ELECTRODES

ELOX B 308 L
( E 308L-15 )

It is an austenitic electrode composed of low carbon alloy core wire and basic coated. It is used in all industries where similar alloy steels are welded, including high carbon steels such as 13% chrome ferritic steels., High ductility of the weld metal, therefore preferably use...

ELOX B 308 H
( E 308H-15 )

A basic coating electrodes are used for welding type 304H and similar applications where creep strength is required, Electrodes are the same as E308 , except for carbon content that has been restricted in the range of 0.04 to 0.08, It provides higher tensile and creep streng...

ELOX R 308 L Mo
( E 308LMo-16 )

A rutile electrode for welding of dissimilar steels, The general purpose electrode for repair welding, It has easy slag removal and smooth appearance in filled welding, These electrodes are recommended for welding ASTM CF3M stainless steel castings, as they match the base metal w...

ELOX RS 308
( E308-26 )

Applicability in joint and surface welding operations of 18/8 CrNi steels, high strength tempered steels, stainless steels and carbon steels., Welding efficiency of approximately 150%., Resistance to high current., Re-drying: 120-200ºC / 2 h.

ELOX R 309 L
( E 309L-16 )

GeKa ELOX R 309L electrodes are widely used in carbon-stainless steel joints. for example, joining mild or low alloy steels with AISI 304., If a service temperature above 370 °C or heat treatment is applied after welding dissimilar steels, embrittlement or cracking may occur. Thi...

ELOX R 309 L-17
( E 309L-17 )

Similar-type austenitic stainless steels, dissimilar metals, buffer layers on mild and low-alloyed steels prior ta build up or overlaying with any stainless electrodes, joining of corrosion resistant stainless steel with mild or low alloy steels, clad steels, Ferrite content...

ELOX R 309 H
( E 309H-16 )

It is used for joining stainless and low alloy steels and for buttering dissimilar steel welds., The carbon restriction will provide higher tensile and creep strengths at elevated temperatures according to ELOX R 309 L, This together with a typical ferrite content of about 6 FN m...

ELOX R 309 MoL
( E 309LMo-16 )

Dissimilar joint welds – overlay welding the first corrosion resistant surface layer on P235GH, P265GH, S255N, P295GH, S355N – S500N and high-temperature quenched and tempered fine-grained steels., Re-drying: 120-200ºC / 2 h., The lower carbon content of the weld metal reduces th...

ELOX R 309 MoL-17
( E 309LMo-17 )

Similar type austenitic stainless steels, dissimilar metals , buffer layers on mild and low-alloy steels prior ta build up or overlaying with any stainless steels electrode, Joining of corrosion-resistant stainless steel with mild or low- alloy steels, clad steels, The lower ca...

ELOX B 309
( E 309-15 )

Basic-coated alloyed core wire electrode for welding analogous, heat resistant rolled, forged and cast steels as well as heat resistant ferritic CrSiAI steels, For weld joints exposed to reducing, sulphurous gases, the final layer has to be deposited by means ELOX B 327, In a...

ELOX R 310
( ~E 310-16 )

Weld metal has the scaling resistance up to +1200°C., The risk of embrittlement should be avoided at operating temperature 650-900 °C. Thick welds should be made with basic electrodes ELOX B 310., Re-drying: 120-200ºC / 2 h., Rutile coated alloyed-core wire electrode for similar...

ELOX R 310 Mo
( E 310Mo-16 )

Rutile-basic coated electrode, The addition of Mo is improved high temperature creep properties, The weld deposit is full austenitic and corrosion resistant

ELOX B 310
( ~E 310-15 )

Austenitic CrNi steels, ferritic CrNiAI alloyed steels, heat-resisting rolled, forged and cast steels used in ceramic, petrochemical industries and furnace, boilers, chimney applications, Weld metal is resistant to working temperature - 196°C up to +1200°C

ELOX R 312
( ~E 312-16 )

Alloyed-unalloyed high-resistant steels, Cr and Mn steels, joint welding of tool steels and different steels and repair welding of sprockets and wheelshaft, Weld metal is resistant to corrosions, cracks and rust, Requirement of re-drying for min. 2 hours at the temperature 300°...

ELOX R 316 L
( E 316L-16 )

Tanks, pipes and equipments made of Cr-Ni-Mo low-carbon steels which are used in food, textile, chemical and paint industries, Weld metal is resistant to acid, corrosion, Serviceability at temperatures up to 400°C, Requirement of Re-drying for min. 2 hours at the temperature 30...

ELOX R 316 L-17
( E 316L-17 )

Rutile-coated low-carbon electrode for use in tanks, pipes and equipments made of Cr-Ni-Mo low-carbon steels which are used in food, textile, chemical and paint industries, Weld metal is resistant resistant to acid, corrosion, Serviceability at temperatures up to 400°C, Require...

ELOX B 316-L
( E 316L-15 )

Low carbon alloyed core wire austenitic electrode with basic coating for use in all industries where analogous steels, including higher carbon grades and ferritic 13% Cr types are welded. High ductility of weld metal, therefore preferably used for welding of heavy sections., N...

ELOX RS 316
( E316-26 )

Used for welding of Cr-Ni-Mo alloyed steels, joint of stainless steel to carbon steels and used for surfacing of stainless steel on carbon steels, The efficiency of weld metal is approx. 150%, It is synthetic electrode and is resistant to high current, Requirement of re-drying...

ELOX R 317 L
( E 317L-16 )

Reduces the possibility of intergranular carbide precipitation, providing increase in resistance to intergranular corrosion without use of stabilizers such as Niobium or Titanium, Rutile coated alloyed-core wire electrode for corrosion resistant CrNi steels of increased Mo-co...

ELOX R 318
( ~E 318-16 )

Used for the welding of tanks and pipes made of Cr-Ni-Mo-alloyed, stabilized steels which are used in food, chemical textile and paint industries, The weld metal stabilized by Nb is resistant to temperatures up to +400°C, Re-drying: 120-200ºC / 2 h.